Metal Cutter Tungsten Carbide Blanks High Elastic Modulus Suitable For Treating Solid Wood
Applications:
The cemented carbide strip is mainly composed of tungsten carbide and cobalt powder, and is formed by metallurgical method by powdering, ball milling, pressing, sintering, fine grinding and polishing. The composition of tungsten carbide and cobalt in different lengths of cemented carbide strips is also different.
Custom processing: blank, fine grinding, punching, beveling, or other drawings to produce and process.
1. Suitable for treating solid wood, shaving board and middle-density fiberboard.
2. Be used to make woodworking tools, such as for mining tool, reamer, serrated knife blade and various blade.
Tungsten Carbide Blanks Specification:
| GRADE | DENSITY g/cm3 | TYPICAL VALUE | APPLICATION SCOPE | |
| HARDNESS | BENDING STRENGTH | |||
| YG3 | 15.10~15.30 | 92.5 | 1700 | Superior wear resistance only less than YG3X, sensitive to impact and vibration, suitable for cast non-ferrous metal and its alloy finish turning, semi-finish turning, thread finish turning and hole expanding. |
| YG3X | 15.10~15.30 | 93.6 | 1450 | Best wear resistance in Tungeten and Cobalt alooy, but not good in anti-impact proprety, suitable for cast iron, non-ferrous and alloy, quenched steel, alloy steel small cutting section machining at high speed. |
| YG6X | 14.80~15.00 | 92.4 | 2000 | Belong to small granule Tungsten carbide alloy, wear resistance higher than YG6. Suitable for machining cold and hard alloy cast iron and heat resistance alloy steel, as well as finish machiing for normal cast iron. |
| YG6 | 14.80~15.00 | 91.1 | 2100 | High wear resistance but less than YG3, better anti-impact and anti-vibration than YG3X, Suitable for cast iron, non-ferrous and alloy, non-metal material semi-finish machining and finish machining. |
| YG6A | 14.8~15.00 | 92.8 | 1850 | Belong to small granule alloy, wear resistance hig, suitable for semi-finish machining of cold and hard cast iron, non-ferrous and alloy, as well as semi-finish machining and finish machining for quenched steel, alloy steel |
| YG8 | 14.6~14.80 | 90.5 | 2300 | High bending strength resistance, better anti-impact and anti-vibration than YG6, suitable for cast iron, non-ferrous and alloy, non-metal material rough machining at low speed. |