Cemented Tungsten Carbide Wear Bars For Wood Working
Applications:
- 100% virgin raw materials, stable chemical properties, long life circle.
- High hardness, good hardness, excellent wear-resistance.
- The heat-conducting property and electrical conductivity of tungsten carbide is close to iron or iron alloy.
- Better overall machining performance in high heat and high speed manufacturing environment.
- Hot Isostatic-Pressing (HIP) results in a greatly increased Transverse Rupture Strength(TRS), provide 20%-30% more on bending strength.
Property
Recommened grade:K20(YG6),K30(YG8),YG15,YG20.
density: 14.5-15.0 g/cm³
HRA: 89-92
T.R.S: 2500-3200 N/m㎡
porosity: A02B00C00
- Grade for China tungsten carbide strip blades/ planer cutting blade / tungsten carbide strips
| GRADE | ISO | DENSITY
(g/cm3) | HARDNESS
(HRA) | TRS
(N/mm2) | NOOE |
| YG6 | K20 | 14.9 | 2150 | 90.0 | Good wear resistance, used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron. |
| YG6A | K05-K10 | 14.9 | 1860 | 92.0 | Has wear resistance higher than YG6, used for processing hard wood, original wood, aluminum section bar, brass rod and cast iron. |
| YG6X | K10 | 14.9 | 2100 | 91.0 | |
| YG8 | (K30) | 14.7 | 2320 | 89.5 | Wear and percussion resistance , used for processing hard wood, soft wood, ferrous and non-ferrous. |
| YG10X | K20-K30 | 14.5 | 2150 | 92.2 | Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous,metal and non-metallid materials. |
| YL10.2 | K30 | 14.5 | 3600 | 92.2 | Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous,metal and non-metallid materials |
| YG15 | K40 | 14.00 | 87.5 | 2800 | |
Other grades of carbide strips may be offered according to customers' requirement.